LMS-S008-CR-DP-290Y/490T Dual Phase — Cold Rolled Steel

LMS-S008-CR-DP-290Y/490T is a dual phase grade cold rolled steel conforming to the lucid material specifications. At 290 MPa minimum yield strength, this is intermediate-strength steel for structural cross-members, seat mounting brackets, and suspension component interfaces, with structural stamping capability for load-carrying components requiring consistent thickness reduction.

As a Dual Phase steel, LMS-S008-CR-DP-290Y/490T offers a specific combination of strength and formability engineered for advanced automotive manufacturing. The dual-phase microstructure of ferrite and martensite provides excellent work hardening and crash energy absorption.

Ameristeel maintains inventory of LMS-S008-CR-DP-290Y/490T in various gauges and widths, available as coils, sheets, or custom blanks. Our ISO 9001:2015 certified processes ensure consistent quality from prototype through production volumes.

Available coating options for LMS-S008-CR-DP-290Y/490T include Uncoated, Galvanized, Electrogalvanized, Galvannealed, Zinc Magnesium, providing corrosion protection and surface preparation suited to your manufacturing process requirements.

LMS-S008-CR-DP-290Y/490T at 290 MPa yield and 490 MPa tensile compares to LMS-S008-CR-DP-330Y/590T (40 MPa lower yield at 330 MPa and 490 MPa vs 590 MPa tensile) and LMS-S008-CR-BH-240Y/340T (50 MPa higher yield at 240 MPa and 490 MPa vs 340 MPa tensile). Selecting the right grade depends on the balance between strength requirements and forming complexity for your specific stamping application.