LMS-S008-CR-DP-700Y/980T Dual Phase — Cold Rolled Steel

LMS-S008-CR-DP-700Y/980T is a dual phase grade cold rolled steel conforming to the lucid material specifications. At 700 MPa minimum yield strength, this is press-hardened-class steel for rollformed safety cage components and structural energy absorbers, with very high tensile properties for peak structural performance in anti-intrusion and rollover protection members.

As a Dual Phase steel, LMS-S008-CR-DP-700Y/980T offers a specific combination of strength and formability engineered for advanced automotive manufacturing. The dual-phase microstructure of ferrite and martensite provides excellent work hardening and crash energy absorption.

Ameristeel maintains inventory of LMS-S008-CR-DP-700Y/980T in various gauges and widths, available as coils, sheets, or custom blanks. Our ISO 9001:2015 certified processes ensure consistent quality from prototype through production volumes.

Available coating options for LMS-S008-CR-DP-700Y/980T include Uncoated, Galvanized, Electrogalvanized, Galvannealed, Zinc Magnesium, providing corrosion protection and surface preparation suited to your manufacturing process requirements.

LMS-S008-CR-DP-700Y/980T at 700 MPa yield and 980 MPa tensile compares to LMS-S008-CR-CP-780Y/980T (80 MPa lower yield at 780 MPa and 980 MPa vs 980 MPa tensile) and LMS-S008-CR-DP-590Y/980T (110 MPa higher yield at 590 MPa and 980 MPa vs 980 MPa tensile). Selecting the right grade depends on the balance between strength requirements and forming complexity for your specific stamping application.