LMS-S008-CR-MS-860Y/1100T Martensitic — Cold Rolled Steel

LMS-S008-CR-MS-860Y/1100T is a martensitic grade cold rolled steel conforming to the lucid material specifications. At 860 MPa minimum yield strength, this is hot-stamped-equivalent steel for critical occupant protection zones and maximum intrusion resistance, with extreme tensile strength for maximum occupant protection performance in the most severe crash scenarios.

As a Martensitic steel, LMS-S008-CR-MS-860Y/1100T offers a specific combination of strength and formability engineered for advanced automotive manufacturing. The predominantly martensitic microstructure delivers the highest strength levels for anti-intrusion and structural reinforcement.

Ameristeel maintains inventory of LMS-S008-CR-MS-860Y/1100T in various gauges and widths, available as coils, sheets, or custom blanks. Our ISO 9001:2015 certified processes ensure consistent quality from prototype through production volumes.

Available coating options for LMS-S008-CR-MS-860Y/1100T include Uncoated, Galvanized, Electrogalvanized, Galvannealed, Zinc Magnesium, providing corrosion protection and surface preparation suited to your manufacturing process requirements.

LMS-S008-CR-MS-860Y/1100T at 860 MPa yield and 1100 MPa tensile compares to LMS-S008-CR-CP-780Y/980T (80 MPa higher yield at 780 MPa and 1100 MPa vs 980 MPa tensile) and LMS-S008-CR-DP-700Y/980T (160 MPa higher yield at 700 MPa and 1100 MPa vs 980 MPa tensile). Selecting the right grade depends on the balance between strength requirements and forming complexity for your specific stamping application.